@MastersThesis{SilvaNeto:2018:CrFiDi,
               author = "Silva Neto, Jos{\'e} Vieira da",
                title = "Crescimento de filmes de diamante CVD de alta ader{\^e}ncia e 
                         baixas tens{\~o}es residuais sobre substratos de WC-Co",
               school = "Instituto Nacional de Pesquisas Espaciais (INPE)",
                 year = "2018",
              address = "S{\~a}o Jos{\'e} dos Campos",
                month = "2018-02-19",
             keywords = "Diamante CVD, ader{\^e}ncia, WC-Co, CVD diamond, adhesion, 
                         Wc-Co.",
             abstract = "A demanda por maiores velocidades de corte e necessidade de 
                         trabalhos de usinagem em ligas n{\~a}o ferrosas e materiais 
                         n{\~a}o convencionais incitou a busca por ferramentas de corte de 
                         melhores propriedades com custo benef{\'{\i}}cio razo{\'a}vel. 
                         O carbeto de tungst{\^e}nio na matriz de cobalto, conhecido como 
                         Widia, {\'e} amplamente utilizado na ind{\'u}stria, n{\~a}o 
                         s{\'o} de usinagem, mas metal-mec{\^a}nica em geral. 
                         Revestimentos de diamante CVD sobre ferramentas deste material vem 
                         sendo alvo de intensa pesquisa devido {\`a}s propriedades 
                         {\'u}nicas que o diamante pode oferecer e a compatibilidade do 
                         material ao processo de deposi{\c{c}}{\~a}o. Um inconveniente a 
                         ser mitigado {\'e} a interfer{\^e}ncia negativa que o Cobalto, 
                         metal ligante utilizado na produ{\c{c}}{\~a}o de ferramentas de 
                         carbeto de tungst{\^e}nio, causa. Dentre as estrat{\'e}gias para 
                         contornar este problema, est{\'a} o tratamento qu{\'{\i}}mico 
                         de duas etapas, que possibilita a deposi{\c{c}}{\~a}o de filmes 
                         de diamante aderentes a estes substratos. Neste trabalho foi 
                         realizado um estudo dos melhores par{\^a}metros de tratamento 
                         qu{\'{\i}}mico e deposi{\c{c}}{\~a}o de diamante. Diversos 
                         tipos de substrato foram testados, com composi{\c{c}}{\~a}o 
                         variando de 3 a 9% de Cobalto inicial e outros carbetos usados 
                         para finalidades espec{\'{\i}}ficas. Para avaliar as melhores 
                         condi{\c{c}}{\~o}es, o desempenho em testes de 
                         indenta{\c{c}}{\~a}o Rockwell foram relacionados com a pureza e 
                         a tens{\~a}o residual dos filmes. ABSTRACT: The demand for higher 
                         cutting speeds and the need of machining work on nonferrous alloys 
                         and non-conventional materials has triggered the search for 
                         cutting tools of better properties with reasonable cost. Tungsten 
                         carbide in Cobalt matrix, also known as Widia, is highly employed 
                         in industry, not only in machining, but for metal mechanic 
                         industry in general. CVD diamond coatings on tools made of this 
                         material have been focus of intense studies due to its unique 
                         properties and the compatibility of the material to the coating 
                         process. A problem to be overcome is the detrimental influence of 
                         Cobalt, the binder metal used in the production of Tungsten 
                         carbide tools,causes. Amongst the strategies to deal with this 
                         problem, is the two step chemical etching of the binder phase, 
                         that makes possible adherent diamond coatings to be applied onto 
                         this substrates. The best parameters on chemical pretreatment and 
                         diamond deposition were studied. Different types of substrate, 
                         varying its composition from 3 to 9% initial Cobalt and other 
                         carbides with specific purposes. In order to evaluate the best 
                         conditions, the performance in Rockwell indentation tests were 
                         correlated with film purity and its residual stress.",
            committee = "Trava-Airoldi, Vladimir Jesus (presidente/orientador) and Machado, 
                         Jo{\~a}o Paulo de Barros and Fraga, Mariana Amorim",
         englishtitle = "High adhesion and low residual stresses CVD diamond films growth 
                         on WC-Co substrates",
             language = "pt",
                pages = "97",
                  ibi = "8JMKD3MGP3W34P/3QD9DSL",
                  url = "http://urlib.net/ibi/8JMKD3MGP3W34P/3QD9DSL",
           targetfile = "publicacao.pdf",
        urlaccessdate = "27 abr. 2024"
}